Q390
作者：上?？颇饘?/span> 時間：2023-12-01 瀏覽：255對應(yīng)牌號：Q390、Grade55[380]、STKT540、15r2CΦ、HS 390D
Q390A化學(xué)成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.035 | ≤0.035 | ≤0.5 | ≤0.1 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 |
Q390B化學(xué)成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.035 | ≤0.035 | ≤0.5 | ≤0.1 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 |
Q390C化學(xué)成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N | ALs |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.030 | ≤0.030 | ≤0.5 | ≤0.1 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 | ≥0.015 |
Q390D化學(xué)成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N | ALs |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.025 | ≤0.030 | ≤0.5 | ≤0.1 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 | ≥0.015 |
Q390E化學(xué)成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N | ALs |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.02 | ≤0.025 | ≤0.5 | ≤0.1 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 | ≥0.015 |
力學(xué)性能：
【抗拉強度】（σb/MPa）
370-580
【伸長率】（δ5/%）
等級 | δ5/% |
A | ≥19 |
B | ≥19 |
C | ≥20 |
D | ≥20 |
E | ≥20 |
【屈服點】（σs/MPa）
厚度（直徑、邊長）/mm | ≤16 | >16～35 | >35～50 | >50～100 |
σs/MPa | ≥390 | ≥370 | ≥350 | ≥330 |
【沖擊吸收功】（Akv（縱向）/J）
等級￤溫度 | +20℃ | 0℃ | -20℃ | -40℃ |
A |
|
|
|
|
B | ≥34 |
|
|
|
C |
| ≥34 |
|
|
D |
|
| ≥34 |
|
E |
|
|
| ≥27 |
特性及應(yīng)用：
綜合力學(xué)性能好，焊接性、冷、熱加工性能和耐蝕性能均好，C、D、E級鋼具有良好的低溫韌性。
船舶、鍋爐、壓力容器、石油儲罐、橋梁、電站設(shè)備、起重運輸機械及其他較高載荷的焊接結(jié)構(gòu)件。